...Abstract This study aims to investigate the electrochemical and corrosion properties of super duplex stainless steel (SDSS) cladded low carbon steel (LCS) manufactured using powder bed fusion selective laser melting (PBF-SLM) technique in 3.56 wt.% NaCl aqueous solution. The PBF-SLM technique...

...Abstract Inhibited erosion-corrosion of low carbon steel material (UNS G10180) was investigated in a CO₂ saturated oil-brine-sand flow. Experimental data for erosion, corrosion, and erosion-corrosion (E/C) were collected using a 3-cell erosion-corrosion flow loop that allows all three...

... of traditional dissolved oxygen scavenger. Abstract This paper summarizes the results of a recent research project comparing laboratory performance of a polyamine-based to a traditional oxygen scavenger-based boiler water treatment. The corrosion of low carbon steel, copper and a copper alloy (admiralty...

.... In the present work, the corrosion current density of a low carbon steel, a pure aluminum, a stainless steel, a Copper-Nickel alloy were obtained in 1M NaOH, 1M KCl, 1M NaCl, 1M H₂SO₄ solutions, respectively. The obtained corrosion data from the optical interferometry technique, as a Zero...

...Abstract The results of a study of corrosion products composition and morphology during the initial stages of rust formation on low carbon steel was carried out in a tropical humid climate (marine-coastal and rural-urban test sites, located in the Gulf of Mexico, in Southeastern Mexico...

...Table I Bath composition used for preparation of different magnetite coated low carbon steel samples. Sample type Na(OH) (g) NaNO₂ (g) NaNO₃ (g) AI(N0₃)₃9H₂0 (g) Cr(N0₃)₃9H₂0 (g) magnetite 200...

...tolyltriazole benzotriazole triazole chlorinated azole halogen resistant azole copper low carbon steel pitting corrosion inhibitor halogenation chlorination environment toxicity chemical feed chemical discharge INTRODUCTION Corrosion is a process that transforms materials to lower...

... storage site. The corrosion performance of AISI 1016 low carbon steel (LCS) in these solutions was evaluated by DC polarization techniques. LCS showed low general corrosion rates with no localized corrosion in deaerated 10X, 100X and 1000X J-13 waters at 25°C. Higher water temperature up to 90°C and 100X...