The current paper presents the results of a one year atmospheric exposure of four stainless steels (SSs) in Kuwait. Flat panels of SSs types UNS S31603, UNS S13895, UNS S31803 and UNS S32101 having various surface finishing conditions were exposed to the atmosphere at five sites. In addition, welded and U-bend panels of UNS S31603 were exposed to the atmosphere at the five sites. Time of wetness (TOW) and chloride deposition rates were measured. The atmospheric corrosivity of the five sites was specified according to ISO 9223 standard. Based on TOW measurements, the atmosphere corrosivity is in the range of low to medium, while based on the chloride deposition rate, the atmosphere corrosivity is in the range of low to high depending upon the closeness of the site to the sea. The panels of SSs were examined visually as well as using optical and scanning electron microscopy. The degree of corrosion attack on the SSs panels varied with the changes in micro climate, surface roughness, and the type of SS, with the welded panels showing the highest degree of corrosion attack. With regard to alloy type, the ranking accurately reflected the molybdenum content with UNS S31803 SS performing better than UNS S31603L, UNS S13895, and UNS S32101 SSs.

Subject
Surface finishing, Atmospheric corrosion, Time of wetness, Marine environments, Sensors, Chloride deposition, Corrosion rate, Metal surfaces, Atmosphere, Roughness, Climate, Deposition rate, Chlorides
Keywords:
Time of wetness, atmosphere corrosivity, surface finishing, chloride deposition rate
© 2015 Association for Materials Protection and Performance (AMPP). All rights reserved. No part of this publication may be reproduced, stored in a retrieval system, or transmitted, in any form or by any means (electronic, mechanical, photocopying, recording, or otherwise) without the prior written permission of AMPP. Positions and opinions advanced in this work are those of the author(s) and not necessarily those of AMPP. Responsibility for the content of the work lies solely with the author(s).
2015
Association for Materials Protection and Performance (AMPP)
You do not currently have access to this content.