The concentration of diffusible hydrogen introduced into steel was measured, and fatigue crack growth tests and fatigue life tests were carried out in sour crude oil containing a high concentration of hydrogen sulfide and under electrolytic hydrogen-charging conditions in neutral solution, using a high strength steel produced by the thermo-mechanical control process (TMCP) and a mild steel which are steels for hull plates. Comparison of the results demonstrated that a very small amount of hydrogen such as that introduced into steel from sour crude oil under atmospheric pressure accelerated the fatigue crack growth in the high ΔK regime and shortened the fatigue life in the high stress range region, but did not shorten the fatigue life in the low stress region. The electrolytic hydrogen-charging condition appeared to be appropriate as a fatigue-crack-growth test environment to simulate sour crude oil. The deterioration of fatigue characteristics of the TMCP high strength steel was similar with that of the mild steel.

Subject
Marine environments, Corrosion fatigue, Hydrogen concentration, Sour environments, Diffusible hydrogen, Fatigue crack growth rate, Hydrogen charging, Sour crude, Steel, Crude, Fatigue, Hydrogen, Oil
Keywords:
fatigue, corrosion fatigue, fatigue life, crack, crude oil, hydrogen sulfide, hydrogen, ship, steel, TMCP
© 1994 Association for Materials Protection and Performance (AMPP). All rights reserved. No part of this publication may be reproduced, stored in a retrieval system, or transmitted, in any form or by any means (electronic, mechanical, photocopying, recording, or otherwise) without the prior written permission of AMPP. Positions and opinions advanced in this work are those of the author(s) and not necessarily those of AMPP. Responsibility for the content of the work lies solely with the author(s).
1994
Association for Materials Protection and Performance (AMPP)
You do not currently have access to this content.