A physico-electrochemical model has been developed to describe intergranular stress corrosion cracking (IGSCC) in sensitized Type 304 stainless steel (SS) in simulated BWR recirculation environments. This model differs from previously reported models in that the internal and external environments are coupled by the need to conserve charge in the system. Thus, solution of Laplace's equation for the external environment, assuming that oxygen reduction on the external surfaces consumes the positive current emanating from the crack mouth, yields a boundary condition for solving Laplace's equation for the internal crack environment. Metal dissolution at the crack tip is described by the slip dissolution model, with the frequency of rupture of the passive film being a strong function of the stress intensity factor. The reduction of oxygen on the external surfaces is described in terms of a general Butler-Volmer equation that incorporates mass transport and charge transport phenomena. In this way, the model incorporates the effects of oxygen concentration, flow rate, and the conductivity of the external environment as well as accounting for the effect of stress on crack growth.

Subject
Environmental cracking, External stress corrosion cracking, External surfaces, Crack growth, Intergranular stress corrosion cracking, Stress intensity, Stress cracking, Oxygen, Risk reduction, Cracks, Stress corrosion cracking, Conductivity, Chloride stress corrosion cracking
© 1990 Association for Materials Protection and Performance (AMPP). All rights reserved. No part of this publication may be reproduced, stored in a retrieval system, or transmitted, in any form or by any means (electronic, mechanical, photocopying, recording, or otherwise) without the prior written permission of AMPP. Positions and opinions advanced in this work are those of the author(s) and not necessarily those of AMPP. Responsibility for the content of the work lies solely with the author(s).
1990
Association for Materials Protection and Performance (AMPP)
You do not currently have access to this content.