CORROSION SCIENCE
Effect of Velocity on Current Density for Cathodically Polarized Steel in Seawater
CORROSION (1999) 55 (2): 115–127.
Electrochemical, Galvanic, and Mechanical Responses of Grade 2 Titanium in 6% Sodium Chloride Solution
CORROSION (1999) 55 (2): 128–138.
Localized Corrosion and Stress Corrosion Cracking Resistance of Friction Stir Welded Aluminum Alloy 5454
CORROSION (1999) 55 (2): 139–150.
Short-Term Deterioration of Polymer-Coated 55% AI-Zn: Part 2 — Impedance Model for Inhibitor-Modified Surface
CORROSION (1999) 55 (2): 151–156.
Inhibition Effects of Inorganic Multivalent Cations on Iron Corrosion in Aerated Sodium Sulfate Solution
CORROSION (1999) 55 (2): 157–165.
Development of an In-Core Stress Corrosion Cracking Test Method and Preliminary Test Results
CORROSION (1999) 55 (2): 166–172.
CORROSION ENGINEERING
Effect of Water on Mechanical Properties and Stress Corrosion Behavior of Alloy 600, Alloy 690, EN82H Welds, and EN52 Welds
CORROSION (1999) 55 (2): 173–186.
Effect of Alloying Elements and Residuals on Corrosion Resistance of Type 444 Stainless Steel
CORROSION (1999) 55 (2): 187–199.
Effect of Induced Alternating Current Voltage on Cathodically Protected Pipelines Paralleling Electric Power Transmission Lines
CORROSION (1999) 55 (2): 200–205.
Impact of Graphite Gasket/Duplex Stainless Steel Couples on Crevice Chemistry and the Likelihood of Crevice Attack in Seawater
CORROSION (1999) 55 (2): 206–212.