Currently, highway/railway bridges are designed for the service life of more than 100 y. In such reinforced concrete structures, fusion-bonded epoxy (FBE) coated steel rebars are being used in anticipation of delayed initiation of reinforcement corrosion. However, the FBE steel rebars get exposed to sunlight/ultraviolet rays during prolonged storage and delayed/staged construction. This paper presents microanalytical and electrochemical data (Fourier transform infrared spectroscopy, scanning electron microscopy, energy dispersion x-ray diffraction, and electrochemical impedance spectroscopy) and shows the adverse effects of sunlight/UV exposure on the corrosion resistance of FBE-coated steel reinforcement in concrete construction. Based on tests on steel-mortar specimens, the mechanisms of UV-induced chemical changes, shrinkage, and cracking of FBE coating, and the resulting steel corrosion mechanisms are proposed. Also, the adverse effects of sunlight/UV exposure on chloride threshold and reduction in the service life of FBE-coated steel in cementitious systems are presented. The paper recommends to minimize the exposure of FBE-coated steel rebars to sunlight/UV rays to less than one month.

Subject
Chloride threshold, Steel surfaces, Coatings, Rebar, Corrosion initiation, Mortar, Fusion bonded epoxy coating, Epoxy coatings, Interfaces, Steel rebar, Steel, Chlorides, Concrete
Keywords:
chloride threshold, concrete, corrosion, epoxy-coating, service life, steel, ultraviolet
© 2020, NACE International
2020
You do not currently have access to this content.