The January 2014 Federal Reduction of Lead in Drinking Water Act reduced the lead content in brass used in water distribution operations and in premise plumbing from 8% to <0.25% Pb (termed “nonleaded”) to protect the public from lead exposure. The switch to nonleaded materials has created legitimate concerns for water utilities, because anecdotally, the new nonleaded alloys have sometimes been more susceptible to erosion corrosion than the older leaded brass alloys. This study investigated the performance of 12 nonleaded alloys vis-à-vis conventional leaded red brass using an ASTM standard cavitation test and an erosion corrosion pipe-loop method. All 12 nonleaded test alloys were more resistant to cavitation than red brass. Silicon brass C87500 had the greatest susceptibility to erosion corrosion, while stainless steel alloys witnessed negligible weight loss and demonstrated superior resistance to erosion corrosion. All other alloys had erosion corrosion damage comparable to (or worse than) the control red brass. This preliminary study is a critical first step toward determining the useful applications of each material in potable water systems, especially for pump impellers and plumbing fittings exposed to high velocity.
Skip Nav Destination
Article navigation
1 April 2019
Research Article|
September 11 2018
Cavitation and Erosion Corrosion Resistance of Nonleaded Alloys in Chlorinated Potable Water
Siddhartha Roy;
Siddhartha Roy
‡
*Civil and Environmental Engineering, Virginia Tech, 418 Durham Hall, 1145 Perry St., Blacksburg, VA 24061.
‡Corresponding author. E-mail: [email protected].
Search for other works by this author on:
Philip A. Smith;
Philip A. Smith
*Civil and Environmental Engineering, Virginia Tech, 418 Durham Hall, 1145 Perry St., Blacksburg, VA 24061.
Search for other works by this author on:
Gregory R. House;
Gregory R. House
*Civil and Environmental Engineering, Virginia Tech, 418 Durham Hall, 1145 Perry St., Blacksburg, VA 24061.
Search for other works by this author on:
Marc A. Edwards
Marc A. Edwards
*Civil and Environmental Engineering, Virginia Tech, 418 Durham Hall, 1145 Perry St., Blacksburg, VA 24061.
Search for other works by this author on:
‡Corresponding author. E-mail: [email protected].
Online ISSN: 1938-159X
Print ISSN: 0010-9312
© 2019, NACE International
2019
CORROSION (2019) 75 (4): 424–435.
Citation
Siddhartha Roy, Philip A. Smith, Gregory R. House, Marc A. Edwards; Cavitation and Erosion Corrosion Resistance of Nonleaded Alloys in Chlorinated Potable Water. CORROSION 1 April 2019; 75 (4): 424–435. https://doi.org/10.5006/2939
Download citation file:
Citing articles via
Suggested Reading
Corrosion of a Waste Energy Sparge Line
CONF_MAR1997
Inhibition of the Effects of Particle Impingement
CONF_APR2002