In this paper, experimental data are compared for an aluminum/copper galvanic system with model predictions from a commercially available software package. The experimental data consisted of optical profilometry measurements of damage accumulation in a bimetallic Al-Cu strip as a function of immersion time in a chloride environment. Model predictions of corrosion rate were accomplished with software that used a solution of the Laplace equation to determine the potential distribution for a mesh of the system. Current density and, ultimately, corrosion rates were determined with this model by correlating the potential at a mesh point with a current density from the experimental potentiodynamic polarization curves for the materials. Although this is a proven method for systems where the anode material is under activation control, this methodology presents a problem for the case of pitting corrosion, such as Al and its alloys in chloride solution. In the case of pitting corrosion, the surface average current density from the polarization curve (i.e., the couple current density) is not equal to the current density at the base of the pit resulting in a model prediction that underestimates the corrosion rate. To overcome this shortcoming, an alternate method for determining the polarization curve for Al is offered from artificial pit electrodes (pencil electrodes) and model predictions using that method are presented.
Skip Nav Destination
Article navigation
1 August 2018
Research Article|
April 04 2018
Experimental Considerations for Modeling Galvanic Corrosion in Aluminum and Its Alloys
Z. Haque;
Z. Haque
*Department of Chemical, Biomolecular and Corrosion Engineering, The University of Akron, Akron, Ohio 44325.
Search for other works by this author on:
B.A. Clark;
B.A. Clark
*Department of Chemical, Biomolecular and Corrosion Engineering, The University of Akron, Akron, Ohio 44325.
Search for other works by this author on:
R.S. Lillard
R.S. Lillard
‡
*Department of Chemical, Biomolecular and Corrosion Engineering, The University of Akron, Akron, Ohio 44325.
‡Corresponding author. E-mail: [email protected].
Search for other works by this author on:
‡Corresponding author. E-mail: [email protected].
Online ISSN: 1938-159X
Print ISSN: 0010-9312
© 2018, NACE International
2018
CORROSION (2018) 74 (8): 903–913.
Citation
Z. Haque, B.A. Clark, R.S. Lillard; Experimental Considerations for Modeling Galvanic Corrosion in Aluminum and Its Alloys. CORROSION 1 August 2018; 74 (8): 903–913. https://doi.org/10.5006/2607
Download citation file:
Citing articles via
Suggested Reading
Electropolymerization and Possible Corrosion Protection Effect of Polypyrrole Coatings on AA1050 (UNS A91050) in NaCl Solutions
CORROSION (April,2019)
Feasibility of the Use of Galvanic Couples to Develop Corrosion Sensors for Reinforced Concrete Structures
CORROSION (April,2019)
Dissolution of Magnetite Coupled with Iron of Various Surface Areas
CORROSION (October,2007)
Corrosion Performance of Concrete Columns After Localized Repairs in a Tropical Coastal Environment
CORROSION (February,2009)