The effect of chloride ion on stress corrosion cracking (SCC) propagation of austenitic stainless steel was investigated by the straining electrode method in 3.36 M NaCl at ambient temperature. It was observed that retardation of anodic dissolution on the crack sides depends on potentials, pH, chloride concentration, and strain rate.