The oxidation kinetics at 900 C (1652 F) of a sulfur impregnated, a Ni-Ni3S2 eutectic coated, and a NaNO3 coated nickel base alloy were studied. It was determined that Na2O/substrate interactions are more influential than sulfur/substrate interactions on the accelerated oxidation phenomena, sulfidation.

Subject
Sulfur, Oxidation kinetics, Precipitates, Nickel based alloys, Chromium, Oxidation behavior, Sodium, Sulfidation, Oxygen, Sulfides, Nickel, Alloys, Oxidation