Corrosion tunnels can form in commercially pure austenitic alloys in the absence of chloride ions and stress corrosion cracking conditions.

Subject
Diffusion, Nickel based alloys, Oxide formation, Oxide films, Chloride ions, Stress, Commercial alloys, Anodic reactions, Intergranular stress, Tunnels, Stainless steel, Grain boundary, Chloride stress corrosion cracking