3.2.2, 6.2.5, 2.3.5, 3.7.3
Intergranular Corrosion Testing by Polarographie Method. (In Japanese). Kazuyoshi Okano, Yukinori Ota and Yoshiharu Kitamura. Corrosion Engineering (Japan), 8, No. 1, 5-6 (1959) Jan.
Bath voltage-ampere curves of various stainless steels in boiling sulfuric acid-copper sulfate solution was measured by a polarographic method. A relationship was found between intergranular corrosion, type of stainless steel and its heat treated condition. 18505
3.2.2, 6.3.6, 3.7.3
An Investigation of Hydrogen Embrittlement in Copper. Einar Mattson and Franz Schuckher. AB Svenska Metallverken, Västerås, Sweden. J. Inst. Metals, 87, Pt. 8, 241247 (1959) April.
Deoxidation and the hydrogen embrittlement of oxygen-bearing copper have been investigated by means of annealing experiments in the range of 400 to 700 C. The effects of hydrogen pressure, annealing temperature, and annealing time were studied. At the beginning of the annealing period, deoxidation unaccompanied by cracking takes place through diffusion of oxygen to the surface (activation...